Title

NANO-STRUCTURE AND ELECTRICAL PROPERTIES OF N+ ION IMPLANTED TITANIUM THIN FILMS AS A FUNCTION OF N+ ION FLUX

Writers

KHOJIER K. | SAVALONI H.

Pages

 Start Page 15 | End Page 19

Keywords

Abstract

 Nitrogen ions of 10 keV with different fluxes ranging from 5 × 1017 to 2 × 1018 ions/cm2 were implanted in Ti thin films of 61.5 nm thickness deposited on glass substrate, by means of electron beam evaporation. X-ray diffraction (XRD) and atomic force microscope (AFM) were used to obtain the crystallographic characteristics and the surface morphology of the samples, respectively. Rutherford Back Scattering (RBS) technique was employed, in order to obtain film thickness and also investigate the N+ ions distribution in Ti thin films. Average electrical resistance of the samples was measured by four point probe method. The results showed that, V-Ti4N3-x phase of TITANIUM nitride is formed with N+ ion implantation, and intensity of this peak increased with N+ ion flux. Furthermore, grain size, surface roughness and average resistance of samples were also increased with N+ flux. RBS spectra of the samples showed that both film thickness and the film density increased with N+ ion flux. An explanation on the ion implanation process is given for this observation.

Cites

  • No record.
  • References

  • No record.
  • Related Journal Papers

  • No record.
  • Related Seminar Papers

  • No record.
  • Related Plans

  • No record.





  • Advertising

    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID
    مرکز اطلاعات علمی SID