INVESTIGATION THE MECHANICAL AND MICROSTRUCTURAL PROPRETIES OF COPPER SURFACE COMPOSITE CU/SIO2 FABRICATED BY FRICTION STIR PROCESSING

 
 
Author(s):  KHODABAKHSHI ELAHE, KAZEMI SHAHAB*, AHMADIFARD SAEED
 
* DEPARTMENT OF MATERIAL ENGINEERING, BU ALI SINA UNIVERSITY, HAMEDAN, IRAN
 
Abstract: 

Friction stir processing (FSP) is a surface improvement method. This process has been developed for facilitating the refinement of microstructure, improving the mechanical properties and producing the surface composite. The aim of this study is producing the surface copper-based nanocomposite with reinforcing SiO2 particles by friction stir processing for improving the mechanical properties. Therefore, 56 mm/min fixed traverse speed and 500, 710, 1000 rpm rotational speeds were used. Microstructures of samples were studied by optical and scanning electron microscopes. Optimum sample had a rotational and traverse speed of 500 rpm and 56 mm/min, respectively. The mechanical properties of the produced surface composite such as microhardness and tensile strength were evaluated and then compared with the base metal. The results of the mechanical tests showed that the microhardness and tensile strength were improved in comparison with base metal. The microhardness of the base metal and optimum sample were about 84Hv and 121 Hv, and tensile strength of them were 218 MPa, and 227 MPa, respectively. Finally, wear properties of surface composite were investigated. The results exhibited better wear behavior and also 28 percent decrease in friction coefficient of produced composite compared with the base metal.

 
Keyword(s): FRICTION STIR, MECHANICAL PROPERTIES, MICROHARDNESS, COPPER, WEAR
 
 
References: 
  • Not Registered.
  •  
  •  
 
Citations: 
  • Not Registered.
 
+ Click to Cite.
APA: Copy

khodabakhshi, E., & KAZEMI, S., & AHMADIFARD, S. (2018). INVESTIGATION THE MECHANICAL AND MICROSTRUCTURAL PROPRETIES OF COPPER SURFACE COMPOSITE CU/SIO2 FABRICATED BY FRICTION STIR PROCESSING. JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC), 4(4 ), 426-433. https://www.sid.ir/en/journal/ViewPaper.aspx?id=573198



Vancouver: Copy

khodabakhshi Elahe, KAZEMI SHAHAB, AHMADIFARD SAEED. INVESTIGATION THE MECHANICAL AND MICROSTRUCTURAL PROPRETIES OF COPPER SURFACE COMPOSITE CU/SIO2 FABRICATED BY FRICTION STIR PROCESSING. JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC). 2018 [cited 2021August01];4(4 ):426-433. Available from: https://www.sid.ir/en/journal/ViewPaper.aspx?id=573198



IEEE: Copy

khodabakhshi, E., KAZEMI, S., AHMADIFARD, S., 2018. INVESTIGATION THE MECHANICAL AND MICROSTRUCTURAL PROPRETIES OF COPPER SURFACE COMPOSITE CU/SIO2 FABRICATED BY FRICTION STIR PROCESSING. JOURNAL OF SCIENCE AND TECHNOLOGY OF COMPOSITES (JSTC), [online] 4(4 ), pp.426-433. Available: https://www.sid.ir/en/journal/ViewPaper.aspx?id=573198.



 
 
Persian Abstract Yearly Visit 50
 
 
Latest on Blog
Enter SID Blog