KINETICS OF CHROMIUM CARBIDE FORMATION ON AISI 1020 STEEL BY TRD PROCESS

 
 
Author(s):  KARIMI ZARCHI H.R., JALALY M., SOLTANIEH M.
 
* 
 
Abstract: 

Using thermal reactive diffusion (TRD) process in order to produce a carbide or nitride layer (such as chromium carbide) onto metals and alloys is one of the techniques for increasing surface hardness and enhancing oxidation, corrosion and wear resistance. In this research, kinetics of chromium carbide coating formation onto AISI 1020 steel by salt bath method at 950, 1000.1050oC for 3- 9 h has been studied. The presence of (Cr, Fe)7C3 on steel surface was shown by XRD analysis. Observations using optical and SEM microscopes from sample cross sections show a rather smooth and compact layer of chromium carbide onto samples surface.
Surface micro hardness of coated steel, measured by Vickers method, is equal to 1350 HV0050KKg. kinetic study of carbide coating, formed by this process, shows firstly a parabolic relationship between carbide thickness and treated time, secondly the activation energy for chromium carbide formation on 1020 steel in borax salt bath is equal to 225.6 KJ/mol. In addition, for predicting carbide layer thickness, contour diagrams are suggested. Yet the possibility of using a series of mathematical equations for predicting carbide thickness from treated time and bath temperature has been discussed.

 
Keyword(s): TRD TECHNOLOGY, BORAX BATH, CHROMIUM CARBIDE COATING, KINETICS, ACTIVATION ENERGY
 
 
References: 
  • Not Registered.
  •  
  •  
 
Citations: 
  • Not Registered.
 
+ Click to Cite.
APA: Copy

KARIMI ZARCHI, H., & JALALY, M., & SOLTANIEH, M. (2008). KINETICS OF CHROMIUM CARBIDE FORMATION ON AISI 1020 STEEL BY TRD PROCESS. JOURNAL OF FACULTY OF ENGINEERING (UNIVERSITY OF TABRIZ), 36(2 (54) MECHANICAL ENGINEERING), 87-92. https://www.sid.ir/en/journal/ViewPaper.aspx?id=277261



Vancouver: Copy

KARIMI ZARCHI H.R., JALALY M., SOLTANIEH M.. KINETICS OF CHROMIUM CARBIDE FORMATION ON AISI 1020 STEEL BY TRD PROCESS. JOURNAL OF FACULTY OF ENGINEERING (UNIVERSITY OF TABRIZ). 2008 [cited 2021July25];36(2 (54) MECHANICAL ENGINEERING):87-92. Available from: https://www.sid.ir/en/journal/ViewPaper.aspx?id=277261



IEEE: Copy

KARIMI ZARCHI, H., JALALY, M., SOLTANIEH, M., 2008. KINETICS OF CHROMIUM CARBIDE FORMATION ON AISI 1020 STEEL BY TRD PROCESS. JOURNAL OF FACULTY OF ENGINEERING (UNIVERSITY OF TABRIZ), [online] 36(2 (54) MECHANICAL ENGINEERING), pp.87-92. Available: https://www.sid.ir/en/journal/ViewPaper.aspx?id=277261.



 
 
Persian Abstract Yearly Visit 54
 
 
Latest on Blog
Enter SID Blog