WATER ABSORPTION AND THICKNESS SWELLING BEHAVIOR OF MEDIUM DENSITY FIBERBOARD MANUFACTURED BY HYDROTHERMALLY TREATED FIBERS

 
 
Author(s):  FALLAH MOGHADAM BEHAMBARI P., MOHEBBY B.*, ILBEIGI F.
 
* 
 
Abstract: 

In this research, water absorption and thickness swelling behavior of hydrothermally modified fiberboard (MDF). Were evaluated Fibers were treated in a stainless steel reactor at temperatures of 120, 150 and 180°C for holding times of 0, 30 and 90 min. Test boards were prepared based on the target density of 0.7g/cm3 at the press temperature of 175°C as well as the pressure of 30 bar and the press time of 5 min. Urea formaldehyde (UF) resin was applied at 10% based on the fibers dry weight. Test samples (10´20´20mm) were cut from the boards, dried in an oven and soaked in the water. Water absorption, thickness swelling and their rates were measured in the soaked samples.
Results revealed that increase of the treatment temperature caused decrease of water absorption and thickness swelling in the treated boards except in samples treated at 120
°C. It was also indicated that increase of the holding time did not significantly affect water absorption and thickness swelling.

 
Keyword(s): HYDROTHERMAL TREATMENT, MEDIUM DENSITY FIBERBOARD (MDF), WATER ABSORPTION, THICKNESS SWELLING
 
 
References: 
  • Not Registered.
  •  
  •  
 
Citations: 
  • Not Registered.
 
+ Click to Cite.
APA: Copy

FALLAH MOGHADAM BEHAMBARI, P., & MOHEBBY, B., & ILBEIGI, F. (2010). WATER ABSORPTION AND THICKNESS SWELLING BEHAVIOR OF MEDIUM DENSITY FIBERBOARD MANUFACTURED BY HYDROTHERMALLY TREATED FIBERS. IRANIAN JOURNAL OF WOOD AND PAPER INDUSTRIES, 1(1), 1-11. https://www.sid.ir/en/journal/ViewPaper.aspx?id=192192



Vancouver: Copy

FALLAH MOGHADAM BEHAMBARI P., MOHEBBY B., ILBEIGI F.. WATER ABSORPTION AND THICKNESS SWELLING BEHAVIOR OF MEDIUM DENSITY FIBERBOARD MANUFACTURED BY HYDROTHERMALLY TREATED FIBERS. IRANIAN JOURNAL OF WOOD AND PAPER INDUSTRIES. 2010 [cited 2021September18];1(1):1-11. Available from: https://www.sid.ir/en/journal/ViewPaper.aspx?id=192192



IEEE: Copy

FALLAH MOGHADAM BEHAMBARI, P., MOHEBBY, B., ILBEIGI, F., 2010. WATER ABSORPTION AND THICKNESS SWELLING BEHAVIOR OF MEDIUM DENSITY FIBERBOARD MANUFACTURED BY HYDROTHERMALLY TREATED FIBERS. IRANIAN JOURNAL OF WOOD AND PAPER INDUSTRIES, [online] 1(1), pp.1-11. Available: https://www.sid.ir/en/journal/ViewPaper.aspx?id=192192.



 
 
Persian Abstract Yearly Visit 124
 
 
Latest on Blog
Enter SID Blog