Journal:   IRANIAN JOURNAL OF ENVIRONMENTAL HEALTH SCIENCE AND ENGINEERING (IJEHSE)   FALL 2007 , Volume 4 , Number 4; Page(s) 263 To 269.
 
Paper: 

SYNTHESIS, ACTIVITY AND THERMAL STABILITY OF GOLD NANOPARTICLE ON MODIFIED NH4-Y TYPE ZEOLITE FOR COOXIDATION

 
 
Author(s):  ASILIAN MAHABADI HASAN*, JAFARI S., KHAVANIN A., KAZEMIAN H.
 
* DEPARTMENT OF OCCUPATIONAL AND ENVIRONMENTAL HEALTH, MEDICAL FACULTY, TARBIAT MODARES UNIVERSITY, TEHRAN, IRAN
 
Abstract: 

Gold nanoparticle is the active catalyst for CO oxidation at low temperature. This feature of gold base catalysts is suitable to overcome the problem of cold-start problem of automobile exhaust TWC converters. In this study gold nanoparticle were deposited on modified NH4-Y type zeolite. The activity of synthesized catalyst was measured in a fixed-bed quartz-tubular reactor (7mm i.d.) under atmospheric pressure. In order to investigate the catalytic activities toward CO oxidation reaction, 31mL/min of air and 0.155mL/min of carbon monoxide were mixed and then passed through the reactor. It was found that activity of Au/Y catalyst was 100% at 20°C. The thermal stability of Au/Y catalyst was measured at 400°C for 4h. The activity of the catalyst was decreased to 65% at 20°C after thermal stability test. Results of Energy Dispersive Analysis by X-rays before and after thermal stability have showed that Au content of these samples were 3.89% and 1.76, respectively. It was found that the amount of Au content decreased after thermal stability process. Fourier Transform Infrared (FT-IR) spectra showed no changes in framework structure of zeolite during thermal stabilization process of the catalyst.

 
Keyword(s): GOLD NANOPARTICLE, NH4Y-TYPE ZEOLITE, CO OXIDATION, CATALYST, THERMAL STABILIZATION
 
 
References: 
  • Not Registered.
  •  
  •  
 
Citations: 
  • Not Registered.
 
+ Click to Cite.
APA: Copy

JAFARI, S., & KHAVANIN, A., & KAZEMIAN, H. (2007). SYNTHESIS, ACTIVITY AND THERMAL STABILITY OF GOLD NANOPARTICLE ON MODIFIED NH4-Y TYPE ZEOLITE FOR COOXIDATION. IRANIAN JOURNAL OF ENVIRONMENTAL HEALTH SCIENCE AND ENGINEERING (IJEHSE), 4(4), 263-269. https://www.sid.ir/en/journal/ViewPaper.aspx?id=101295



Vancouver: Copy

JAFARI S., KHAVANIN A., KAZEMIAN H.. SYNTHESIS, ACTIVITY AND THERMAL STABILITY OF GOLD NANOPARTICLE ON MODIFIED NH4-Y TYPE ZEOLITE FOR COOXIDATION. IRANIAN JOURNAL OF ENVIRONMENTAL HEALTH SCIENCE AND ENGINEERING (IJEHSE). 2007 [cited 2021June25];4(4):263-269. Available from: https://www.sid.ir/en/journal/ViewPaper.aspx?id=101295



IEEE: Copy

JAFARI, S., KHAVANIN, A., KAZEMIAN, H., 2007. SYNTHESIS, ACTIVITY AND THERMAL STABILITY OF GOLD NANOPARTICLE ON MODIFIED NH4-Y TYPE ZEOLITE FOR COOXIDATION. IRANIAN JOURNAL OF ENVIRONMENTAL HEALTH SCIENCE AND ENGINEERING (IJEHSE), [online] 4(4), pp.263-269. Available: https://www.sid.ir/en/journal/ViewPaper.aspx?id=101295.



 
  pdf-File
Yearly Visit 42
 
 
Latest on Blog
Enter SID Blog